Pitting Corrosion Resistance of Ta-Bearing Duplex Stainless Steel

抄録

The effect of Ta addition on the pitting corrosion resistance of duplex stainless steels was investigated in both cases without and with deoxidization/desulfurization by the addition of Al and Ca. The pitting corrosion resistance was improved by the addition of Ta with two proposed mechanisms. For steels without Al and Ca, the MnS inclusions which act as initiation sites of the pitting corrosion are modified to the electrochemically-stable (Ta,Mn) oxysulfides. For steels with Al and Ca, the pitting initiation sites (CaS and (Al,Ca)oxides) are coated with the stable Ta-containing nitrides resulting in the suppression of pitting corrosion propagation.

 

This Paper was Originally Published in Japanese in Zairyo-to-Kankyo 69 (2020) 237–245.

Fig. 11 Schematic illustration of pitting corrosion process of (a) steel without Ta, (b) Ta-bearing steel without Al and Ca, and (c) Ta-bearing steel with Al and Ca.