Production of Nanocrystalline (Fe, Co)-Si-B-P-Cu Alloy with Excellent Soft Magnetic Properties for Commercial Applications

Abstract

With the aim of applying to a magnetic core material, the effect of ribbon thickness on the magnetic properties of a (Fe, Co)-Si-B-P-Cu alloy ribbon was investigated. It is found that the Si addition in (Fe, Co)-Si-B-P-Cu nanocrystalline alloy increased the saturation magnetic flux density (B_s), but degraded the coercivity (H_c), suggesting that the Si addition should be suppressed to a little amount. It is also found that the replacement of Fe with Co is quite effective for obtaining better magnetic properties of Fe-Si-B-P-Cu alloy. Even for the thicker ribbons exceeding 30 µm in thickness, the nanocrystalline Fe_81.2Co₄Si_0.5B_9.5P₄Cu_0.8 alloy exhibited low H_c of 7 A/m and high B_s of 1.84 T. Such excellent magnetic properties were successfully reproduced in 50 mm wide ribbons. This regards that the nanocrystallized Co-containing alloy has high applicability to high-efficiency magnetic core material.