2000 年 49 巻 5 号 p. 260-265
Instability of peak 4 in LiF: Mg, Ti (TLD-600/700) was experimentally examined by comparing the glow curves obtained for 137Cs γ-rays and Fe-ion beam. After post-annealing at 100°C×30min, thermoluminescence (TL) intensity around peak 4 notably decreased only for γ-ray irradiation. In Fe-ion irradiated samples, post-annealing effects were scarcely observed in the TL intensities in the peak-4 region. These results suggest that the peak-4 luminescent centers are unstable and more vulnerable than other peaks to highly-dense ionization.