被服材料の表面特性に関する研究

(第13報) ―一軸及び多軸伸長による織物の表面反射挙動―

抄録

In the previous papers, Parts 5-9, 11 and 12, investigations were made of the influence of uniaxial tensile deformation on the change of surface reflection and crimp properties of fabrics by the two- and three-dimensional goniophotometric methods. Clothing materials generally undergo the multiaxial stretching at the parts of knees and elbows. Then, an investigation has been made of measuring the influence of multiaxial tensile deformation on the behaviour of surface reflection and crimp properties by using a goniophotometer provided with a multiaxial stretchmeter experimentally manufactured.
The results obtained are as follows. The multiaxial stretching of filament fabrics has slightly increased the intensity of regular reflection. The crimp angle increases in warp yarn and decreases in weft yarn, but they never reach zero degree even if the fabric has been highly extended far over crimp percentage. These changes of the intensity of reflection and crimp properties have caused that the fibers in yarn do not straightened and not flattened in order to occure the increase in forces acting at the intersections by multiaxial tensile deformation.
前報 (第5～9, 11, 12報) までは, 一軸伸長変形による織物の表面反射挙動について検討したが, 織物はひじやひざ部などにおいて一軸伸長変形のみならず多軸伸長変形をうけることが多い.
本研究は平面円状に多軸伸長できる装置を試作して, 一軸伸長の場合と同様に変角光度計に取付け, 多軸伸長による表面反射とクリンプの挙動を一軸伸長と比較して検討した.その結果, 多軸伸長において, たて・よこ共クリンプ率の小さい織物では, 初期伸長時から交錯圧が生じてくるため反射光量はわずかに増加するのみであり, クリンプ角はクリンプ率以上の高伸長を与えても真直ぐにならず, ある程度クリンプ角を保つことが認められた.また, 一方にクリンプ率の大きい加工糸を用いた織物では特異な反射挙動を示す.これらの多軸伸長と一軸伸長による表面反射挙動の比較から・無撚り長繊維糸織物の伸長変形による反射光量の増加は, クリンプ率が0となる前後の繊維束の配列性にもとづくことが明らかとなった.