Semitransparent Organic Solar Cells with Polyethylenimine Ethoxylated Interfacial Layer Using Lamination Process

抄録

Semitransparent organic solar cells were fabricated using lamination process. The devices were realized by using two independent substrates with transparent indium-tin-oxide electrode. One substrate was coated with poly(ethylenedioxy-thiophene)/poly(styrenesulfonate) layer and active layer of poly(3-hexylthiophene-2,5-diyl) (P3HT) and (6,6)-phenyl-C61 butyric acid methyl ester mixture. Another substrate was coated with ultra-thin polyethylenimine ethoxylated. The two substrates were laminated using hot press system. The device exhibited semitransparency and showed typical photovoltaic characteristics with open voltage of 0.59 V and short circuit current of 2.9 mA/cm².