Characterization and Phosphate Adsorption Capability of Novel Nickel–Aluminum–Zirconium Complex Hydroxide

抄録

In this study, the adsorption capability of phosphate ion using a novel tri-metals complex hydroxide was evaluated for preventing the eutrophication in water environment. A nickel–aluminum–zirconium complex hydroxide (NAZ) was synthesized using each inorganic sulfate mixing ratio of 0.9 : 1.0 : 0.1 and was calcined at different temperatures. The characteristics of the NAZ were analyzed by scanning electron microscopy images, X-ray diffraction analysis, elemental distribution, and binding energy. Moreover, the amount adsorbed of phosphate ion onto uncalcined and calcined NAZ was measured. That of phosphate ions onto the uncalcined was the largest of all. These results suggested that the adsorption of phosphate ions tends to depend on the physicochemical properties (e.g., amount of hydroxyl groups, pore volumes, and pH) of the adsorbents. Moreover, the adsorption mechanism of phosphate ions was evaluated on the basis of binding energy and elemental analysis. After adsorption, the binding energy of phosphorus P (2s and 2p) peaked and the sulfur peak intensity S(2s) reduced. This result indicated that the adsorption mechanism of phosphate would be exchanged with sulfate ions.