Abstract
The purpose of the present study was to evaluate the effect of dual-peak LED on the polymerization of coinitiator-containing composite resins. For this, microhardness, degree of conversion (DC), and polymerization shrinkage were evaluated. Specimens (coinitiator-containing: Aelite LS Posterior, Tetric EvoCeram, and Vit-l-escence; only camphorquinone-containng: Filtek Z350 and Grandio) were light cured using a quartz-tungsten-halogen (QTH: OP), a single-peak light-emitting diode (LED) (L. E. Demetron: DM), and a dual-peak LED (G-light: GL), respectively. All specimens light cured using GL showed the highest microhardness both on the top and bottom surfaces compared with the values obtained using the rest light-curing units (LCUs). DC had no consistent trend correspond to the LCU, but rather product specific. OP yielded the lowest polymerization shrinkage on the specimens. The coinitiatorcontaining composite resins achieved the highest microhardness by the dual-peak LED (GL). However, the influence of GL on DC and polymerization shrinkage of the specimens was not consistent.