2012 Volume 31 Issue 5 Pages 724-728
This study aimed to develop a dental investment for titanium casting. ZrO2 and Al2O3 were selected as refractory materials to prepare three investments (Codes: A-C) according to the quantity of Zr. Al2O3 cement was used as a binder at a ratio of 15%, they were mixed with special mixing liquid. B1 was used as a control mixed with water. Fundamental examinations were statistically evaluated. A casting test was performed with investment B. Fluidities, setting times, and green strengths showed no remarkable differences; however, they were significantly different from those of B1. Expansion values for A, B, C, and B1 at 850°C were 1.03%±0.08%, 1.96%±0.17%, 4.35%±0.23%, and 1.50%±0.28%, respectively. Castings were covered by only small amounts of mold materials. The hardness test showed no significant differences between castings from B and the ones from commercial investments. The experimental special mixing liquid effectively reduced the water/powder ratio and improved the strength and thermal expansion.