2020 Volume 39 Issue 1 Pages 12-23
This review describes low temperature degradation (LTD), discoloration, and erosion of high translucent dental zirconia and discusses its chemical durability in comparison with other CAD/CAM materials. The LTD of zirconia strongly depended on the firing temperature, yttria content, surface treatment, and heat treatment. Glass ceramics for CAD/CAM were remarkably etched in a lactic acid at 60°C, KOH solution at 60°C, and saline solution at 90°C, whereas zirconia showed no changes in these solutions. Glass ceramics and hybrid resins for CAD/CAM showed significant discoloration in a red wine and rhodamine B solution at 37°C, whereas zirconia showed no discolorations in either solution. It was concluded that high translucent dental zirconia has the highest chemical durability among dental CAD/CAM materials.