Basic properties of novel S-PRG filler-containing cement

抄録

This study was aimed to evaluate the effect of a novel surface pre-reacted glass-ionomer (S-PRG) filler-containing cement for root caries. We prepared the cements using five different S-PRG filler amounts (0, 10, 20, 30, and 40 wt%). Compressive strength, ion release, acid buffering capacity, and microstructure of the as-prepared cements were evaluated. The compressive strength was statistically significant; it was highest for 0 wt% S-PRG cement. Ion release in 0 wt% S-PRG was highest for F⁻ and Al, whereas in 40 wt% S-PRG it was highest for B. For 20, 30, and 40 wt% S-PRG cements, Na and Sr release was higher compared to the other ions. The acid buffering capacity was significantly higher in the 40 wt% S-PRG cement than in the others. In the microstructural analysis, no difference of surface structure was observed among each of the S-PRG filler contents (0–40 wt% S-PRG).