Effect of bioglass and silica coating of zirconia substrate on its bond strength to resin cement

抄録

This study aimed to assess the effect of bioglass and silica coating of zirconia substrate on its bond strength to resin cement. A total of 120 specimens were used in this in-vitro, experimental study. Zirconia discs measuring 10×7×2 mm were cut from Y-TZP zirconia blocks, sintered, cleaned and received different surface treatments of sandblasting, bioglass powder coating+etching, bioglass powder coating+etching+silanization, bioglass slurry coating+etching, bioglass slurry coating+etching+silanization, silica coating+silanization, silica coating+etching+silanization and no treatment group (control). Then the microshear bond strength testing and scanning electron microscope (SEM) analysis were done. Data were analyzed using the Mann Whitney U and the Kruskal Wallis tests. Significant differences existed in bond strength of different groups (p<0.001). The sandblasted and bioglass coated groups showed higher and the colloidal silica-coated groups showed lower bond strength compared to the control group.