Effectively improved 3-dimensional structural stability of atelocollagen-gelatin sponge biomaterial by heat treatment

抄録

Atelocollagen-gelatin (ACG) sponge was fabricated from atelocollagen and gelatin by lyophilization without introducing toxic substances. This study aimed to investigate the effects of heat treatment on the 3-dimensional structural stability of ACG sponge biomaterial. ACG sponge samples were fabricated and heat treated at 125^oC for 12 h in the vacuum. The results revealed that heat treatment did not affect porosity, pore size and mechanical compressive strength. Heat-treated ACG sponge showed decreased absorbance and peak shift of amid I (C=O) stretches, slightly higher water uptake degree and significantly decreased in vitro degradation rate. Moreover, heat-treated ACG sponge maintained good 3-dimensional surface morphology and porous microstructure throughout 7 days, while non-heat-treated ACG sponge collapsed in less than 24 h. The human mesenchymal stromal cells (hMSCs) were shown to adhere and grow well on heat-treated ACG sponges. These results indicate that heat treatment is effective and safe to stabilize 3-dimensional ACG sponge biomaterial for tissue engineering.