1991 年 99 巻 1155 号 p. 1156-1158
A SiC/Al2O3 composite sheet was prepared from a green sheet composed of polycarbosilane (PCS) and Al2O3 powder with the weight ratio of 2:1. The green sheet was fired in the temperature range of 1200° to 1400°C under N2 gas atmosphere, and three point bending strength of the composite was examined. The strength in room temperature increased with firing temperature and showed the maximum value of 333MPa at 1300°C. Dispersion of Al2O3 particles in the SiC matrix was effective to increase the strength of monolithic SiC sheet derived from PCS. When the composite was fired at 1400°C, however, the bending strength dropped rapidly in a similar manner as PCS-derived SiC fiber.