Effect of priming agents on shear bond strengths of resin-based luting agents to a translucent zirconia material

抄録

Purpose: The purpose of the present study was to evaluate the effect of priming agents and artificial aging with thermocycling on shear bond strengths of two resin-based luting agents to a translucent zirconia material.

Methods: A total of 308 pairs of translucent zirconia disk specimens were divided into seven treatment groups: Alloy Primer (ALP), Clearfil Ceramic Primer Plus (CCP), Meta Fast Bonding Liner (MFB), MR. bond (MRB), Super-Bond PZ Primer Liquid B (PZB), V-Primer (VPR), and an unprimed group (UP). The specimens in each group were bonded with Panavia V5 Universal (UNI) and Opaque shade (OPA). Shear bond strengths (n = 11 each) were tested before and after 5000 thermocycles. The data were analyzed with the Kruskal–Wallis test and the Steel–Dwass test.

Results: For both 0 and 5000 thermocycles, the ALP (47.8 and 41.5 MPa, respectively) and CCP (45.8 and 42.3 MPa, respectively) groups showed significantly higher bond strengths than other groups in the UNI luting agent. For the OPA luting agent, CCP group (45.8 MPa) exhibited the highest pre-thermocycling bond strength in all groups. The ALP (32.4 MPa) and CCP (36.5 MPa) groups had significantly higher postthermocycling shear bond strengths than other groups. In several groups, the shear bond strengths of the UNI luting agent were significantly higher than those of the OPA luting agent before and after thermocycling.

Conclusions: Application of priming agents containing hydrophobic phosphate monomer (MDP) yielded the durable bond strengths of resin-based luting agents to a translucent zirconia material.