抄録
Purpose: This study aims to evaluate the effects of cement shade, restorative material type, and thickness on the final color of resin-matrix ceramics.
Methods: Ninety A2 shade resin-matrix ceramic specimens were prepared from Vita Enamic, GC Cerasmart, and Lava Ultimate at 0.5 and 1.0 mm thicknesses. Sixty resin cement disks were fabricated from different shades (A1, A3O, B05, and TR) of RelyX Ultimate at 0.1 mm thickness. CIE color coordinates were measured using a spectrophotometer, and color differences (∆ E 00 ) were calculated. Data were statistically analyzed (P =0.05).
Results: The ΔE 00 values were influenced by the cement shade, restorative material type, thickness, and their interactions ( P < 0.05). A3O cement caused clinically unacceptable values for all groups at 0.5 mm thickness and GC at 1.0 mm thickness. A1 and TR cement shades demonstrated visually perceptible but clinically acceptable values, except for VE-A1 and LU-A1 at 0.5 mm thickness. The ∆E 00 values of the B05 cement shade were lower than the visually perceptible threshold for both thicknesses except for GC at 0.5 mm thickness.
Conclusions: The shade of the resin cement and the type and thickness of the resin-matrix ceramic material significantly affected the resulting final color. To provide a shade matching with natural dentition and to obtain esthetic restorations, especially for the anterior teeth, the resin cement shade and resin-matrix ceramic material should be carefully selected.