Effect of different zirconia surface pretreatments on the flexural strength of veneered Y-TZP ceramic before and after in vitro aging
Eleni SiarampiKatia SarafidouLambrini PapadopoulouNikolaos KantiranisEleana Kontonasaki Petros Koidis
著者情報
ジャーナル オープンアクセス 早期公開

論文ID: JPR_D_21_00067

この記事には本公開記事があります。
詳細
抄録

Purpose: The investigation of zirconia core surface pretreatments on the flexural strength of bilayered zirconia ceramics before and after artificial accelerating aging.

Methods: Ninety bar-shaped specimens were manufactured from Yttria Stabilized Tetragonal Zirconia Polycrystal (Y-TZP) and divided in three groups depending on zirconia surface pretreatment before veneering: layering with liner, pretreatment with silane-containing gas flame (SGF) with the Silano-Pen device and alumina air-abrasion. Half of the veneered specimens in each group (n=15) underwent artificial accelerating aging. A 4-point bending test was performed to determine flexural strength. Three specimens from each group were further analyzed using Scanning Electron Microscopy (SEM), X-ray Diffraction (XRD) and Fourier Transform Infrared Spectroscopy (FTIR) before veneering and after fracture (aged and non-aged subgroups).

Results: Alumina air-abrasion was correlated to increased phase transformation from tetragonal to monoclinic zirconia phase. Qualitative analysis revealed that with the majority of the specimens pretreated with the silane-containing gas flame, areas of the veneering material remained firmly attached to the zirconia core after flexural strength testing. There was no statistically significant difference on the flexural strength among the groups before or after aging. Artificial accelerating aging resulted in statistically significant higher flexural strength of the specimens after aging.

Conclusion: SGF pretreatment can be an acceptable and feasible alternative method before the veneering of Y-TZP zirconia as it presented slightly higher bond strength compared with alumina air-abrasion which was associated with higher tetragonal to monoclinic (tm) phase transformation. Accelerating aging leads to an increase of the mechanical properties under in vitro conditions.

著者関連情報
© 2021 Japan Prosthodontic Society

This is an open-access article distributed under the terms of Creative Commons Attribution-NonCommercial License 4.0 (CC BYNC 4.0), which allows users to distribute and copy the material in any format as long as credit is given to the Japan Prosthodontic Society. It should be noted however, that the material cannot be used for commercial purposes.