アルカリ環境下における鉄系腐食生成物の生成プロセスおよびコンクリート中における鉄筋の腐食環境
高谷 哲奥野 翔矢本田 正和川上 圭司左藤 眞市羽村 陽平山本 貴士宮川 豊章
著者情報
ジャーナル フリー

2017 年 66 巻 8 号 p. 545-552

詳細
抄録

When reinforcement in concrete corrodes, cracks are induced in cover concrete because volume of corrosion products are much larger than that of original steel. Because these cracks can be the index of corrosion grade, many researchers have studied about the relationship between crack width and corrosion weight loss. Recently, it was reported that corrosion products have large influence on the relationship because each corrosion products have its own density and volumetric expansion ratio. However, formation process of corrosion products in alkaline environment have not been made clear and at this point it is difficult to predict corrosion products formed in concrete in various environment. Then in this study, in order to make clear formation process of corrosion products in alkaline environment, corrosion products formed in solution of various OH- and Cl- concentration were evaluated by Raman spectroscopy. And additionally, influence of dissolved oxygen on corrosion products was also investigated. Furthermore, arrangement of corrosion environment of reinforcement in concrete was tried, based on field study.

著者関連情報
© 2017 日本材料学会
次の記事
feedback
Top