Manganese Dissolution from Lithium Doped Li-Mn-O Spinel Cathode Materials into Electrolyte Solution

抄録

Manganese dissolution from spinel LiMn₂O₄ cathode material is one of the origins of a significant capacity fading with cycling for rechargeable lithium ion batteries. To suppress the manganese dissolution, the Li_1+xMn_2−xO₄ (0 ≤ x ≤ 0.1) spinels were prepared. Their cycle performances and the amount of manganese dissolution from the spinels in charged state into an electrolyte were investigated to confirm that the manganese dissolution was suppressed in the lithium-doped spinels system. As a result, it was found that the rate of manganese dissolution decreased and the cyclability was improved with increasing doping amount of lithium in the spinel compound due to stabilizing the spinel structure by substituting lithium for manganese in 16d sites.