In order for Bi2212 superconductors to exhibit good transport properties, they must be sintered at a high temperature, usually around 860℃. If the sintering temperature is too high, the performance of the superconductor will be deteriorated by the diffusion of the substrate components into the sample when the superconductor is applied to electronic devices. Therefore, we investigated the effect of calcination conditions on the transport properties of low-temperature sintered Pr-doped Bi2212 superconductor, aiming to prepare samples at a lower temperature (700℃) than in previous studies by controlling the number of sintering cycles.　　　 In this study, the composition of Bi2.05Sr1.89Ca1.06Cu2Li0.15Oy and Pr2O3 were added as additives, and the samples were sintered at 700℃ for one, two, and three times of calcination, respectively, and the resistivity temperature characteristics, crystal structure, and carbon concentration of the samples were measured. As a result, the sample calcinated one time showed no zero resistance, and the critical temperatures of the samples calcinated two and three times were 56K and 68K, respectively. The crystal structure of the sample sintered at 700℃ showed peaks similar to those of normal Bi2212. Furthermore, the amount of carbon in the samples decreased as the number of times of calcination was increased.

抄録全体を表示

We have fabricated cylindrical and pipe-shaped Bi2212 superconductor samples using Melt-Casting Process. The purpose of this research is to create a superconductor with high-quality transport properties, based on the idea that if a hole is made in the cylinder to form a pipe, the surface area of the sample increases, making it easier for the reaction to proceed during sintering. First, two superconductors with the same composition ratio of Bi2212 but different shapes were fabricated simultaneously. Then, (a) crystal structure, (b) composition ratio, (c) critical temperature, and (d) critical current of the fabricated cylindrical and pipe-shaped samples were measured and compared. In (a), the X-ray diffraction pattern and lattice parameter confirmed that a superconductor sample with the Bi2212 structure can be fabricated using MCP. In (b), the amount of impurity carbon was lower in the pipe-shaped sample, suggesting that the pipe-shaped sample had a larger surface area, which allowed sufficient reaction with oxygen during sintering. In (c), the pipe-shaped sample had a higher critical temperature, but the difference was not significant. In (d), it was found that the critical current density was higher in the pipe-shaped sample. The ratio of the superconducting phase is large, and it is considered that the material became a uniform superconductor.

抄録全体を表示

The calculation of response and limit Strength for traditional Japanese wooden structure often causes the structure collapse at 1st floor. To prevent the structure collapse at a given floor, the equation of every story deformation angle is required. The continuous column of heavy timber over than 180 mm square is proposed to average story deformation angles. In this paper, the calculation method for the section size of continuous columns is proposed. Results are as follows: 1) The calculation method for the section size of continuous columns consists of 2 equations: the equation for flexure capacity and the equation of difference between deformation angles. 2) The proposed method lessens the negative gradient of a Sa-Sd curve.

抄録全体を表示

2017年度に学生寮でインフルエンザ感染爆発が生じたことを契機として，2018年度から学生寮において，学生を主体とする健康教育を試行している．実施プロトコルとしては次のとおりである：学生寮において直面している健康問題について，担当の指導寮生たちが学習・共有し，5〜10分程度の健康教育コンテンツにまとめ，これを学生寮の定例集会で公開する．2022年度に実施された健康教育におけるコンテンツの視聴後アンケートから，このような形の健康教育は視聴者の自己効力感を高めるのに有効であることがわかった．特に，普段から低学年寮生の世話役・相談役である指導寮生が健康情報の提供者となることで，次の３つの効果が得られているようである：１）視聴者の「聴く意識」の向上，２）「楽しく知れる」コンテンツの実現，３）「自分もできる」といった自己効力感の向上．

抄録全体を表示

将来的に活用できる学力育成を目的に，原理や概念に向き合う授業の仕組みづくりを行った．講義，課題，試験が相関するように，それぞれに原理や概念に向き合うための仕掛けを施した．特に，コラムの活用，及び課題の構成や運用の工夫により，これまで行ってきた授業と比べて，主体的に取り組む学生が増加した．また，国立高等専門学校機構が主催するCBT試験結果の分析から，本コンセプトに基づき構築した授業の教育効果が確認された．

抄録全体を表示

複素数は体であり，２行２列の行列で表現できる．複素数は２元数（実数２つの組み合わせで出来る数） の仲間であり，体を環（可換環）に緩めると，２元数は，複素数，分解型複素数，２重数に分類される．研 究紀要 [1] では，可換環である分解型複素数を変数とする関数の微分可能条件であるコーシー・リーマンの 関係式を一般化した．研究紀要 [2] では，３次方程式を利用してオイラーの公式を２変数に一般化し，２変 数の３次曲面関数を定義した．そして，この関数は２変数の加法定理が成り立つことを示した．このノート では，３つの実数の組み合わせで表現される３元数を導入し，これを変数とする関数の微分可能条件を求め， これがコーシー・リーマンの関係式の一般化であることを示す．

抄録全体を表示

加法定理を持つ関数には三角関数や双曲線関数があり，研究紀要 [1] では，これを一般化し，２次曲線関 数を導入した．研究紀要 [2] では，３次方程式 ¸ 3 = 1 によりオイラーの公式を一般化し，２変数３次曲面 関数を導入した．この３次方程式は，１つの実数解と２つの虚数解を持つ．そして，この関数には２変数の 加法定理があり，連立偏微分方程式を満たす．そして，媒介変数は体積という幾何学的な意味を持つ．この ノートでは，研究紀要 [2] を一般化し，３つの実数解を持つ３次方程式を使ったオイラーの公式を考察する． ここでは ¸ = 1; 2; 3 を解に持つ場合を考察する．そして，このオイラーの公式から新しい２変数の３次曲面 関数を定義する．この関数は２変数の加法定理を満たし，ある種の連立偏微分方程式を満たす事を示す．

抄録全体を表示

著者はこれまでの研究で，ある種の連立非線形微分方程式を考察し，その中に解けるモデルが数多く存 在することを示してきた [1, 2, 3]．そして，可積分系の方程式の中に，複素数の構造や可換環の構造が隠れ ていることを示した [2, 3]．このノートでは，２つのパラメータを持つ２種類の連立非線形微分方程式を考 察する．どちらの連立非線形微分方程式も可積分となるが，背後に存在する可積分構造が異なる．そして， 可積分性の背景には体や可換環などの代数的な構造が隠れていることを示す．

抄録全体を表示