Masahiko Morinaga
2016 Volume 57 Issue 3 Pages
213-226
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 15, 2016
JOURNAL
FREE ACCESS
A molecular orbital approach to alloy design has recently made great progress. It is based on the electronic structure calculations by the DV-Xα cluster method, and new alloying parameters are obtained for the first time from the calculations. A theory for alloy design relevant to transition-metal based alloys have been developed using alloying parameters. For example, New PHACOMP has been developed in order to predict the formation of harmful and brittle phases (e.g., σ phase) in nickel-based superalloys. A universal relation has also been discovered between electron density minima and atomic (or ionic) radii in various materials from a series of molecular orbital calculations. Furthermore, another electronic approach is explained focusing on the energy expression of the chemical bond between atoms in hydrides and hydrocarbons. All the hydrides and hydrocarbons are located on an atomization energy diagram, despite the significant differences in the nature of the chemical bond among them. One of the applications of this approach is the catalyst design. The catalytic activities of metal oxides (e.g., Nb
2O
5) are evaluated quantitatively on the dehydrogenation reaction of magnesium hydride (MgH
2), MgH
2 → Mg + H
2.
View full abstract
-
Shigekazu Morito, Yuki Iwami, Tamotsu Koyano, Takuya Ohba
2016 Volume 57 Issue 3 Pages
227-232
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: November 13, 2015
JOURNAL
FREE ACCESS
Microstructures of lath martensite that contains bcc or bct martensite crystals in Fe–C alloys are known to depend on the carbon content of the alloys. The effect of nitrogen content on microstructure, however, has not yet been elucidated. This study elucidates the effects of carbon and nitrogen content on microstructures via local crystallographic analysis. We found that the packet sizes are similar when the nitrogen content in the alloys are the same as the carbon content, with the packet size decreasing with increasing carbon and nitrogen content. The block and sub-block thicknesses in low nitrogen lath martensite are smaller than those in low carbon lath martensite, whereas those in medium and high carbon and nitrogen lath martensites are similar. Martensite lath thickness and dislocation density in the Fe–N alloy laths are lower than those in the Fe–C alloys laths, and the distribution of misorientation angles between adjacent the blocks and sub-blocks in Fe–N alloys is similar to that in Fe–C alloys.
View full abstract
-
Takeshi Teramoto, Masaki Tahara, Hideki Hosoda, Tomonari Inamura
2016 Volume 57 Issue 3 Pages
233-240
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: November 13, 2015
JOURNAL
FREE ACCESS
The kinematic compatibility (KC) between habit plane variants (HPVs) was numerically analyzed and classified in Ti-25Ni-25Pd alloy. There are six distinct types of HPV pair that can satisfy the KC condition at averaged junction plane (JP) between twinned HPVs. By analyzing the KC condition between lattice correspondence variants (CVs) in the HPVs, it was found that there are three types of HPV pair in which all the CVs can be compatible due to the existence of the common rotation to keep the KC at all JPs simultaneously. On the other hand, it was found that the incompatibility inevitably remains in the morphologies known as spear (wedge), folk and herring-bone.
View full abstract
-
Yuki Namigata, Yuki Hattori, M. Imran Khan, Hee Young Kim, Shuichi Miy ...
2016 Volume 57 Issue 3 Pages
241-249
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: November 27, 2015
JOURNAL
FREE ACCESS
Effects of aging on martensitic transformation temperature, microstructure and shape memory characteristics were investigated for Ti
50Ni
20Pd
30 and Ti
52Ni
18Pd
30 alloys. There was no significant change in the microstructure and transformation temperature by aging, irrespective of aging temperature, in case of the Ti
50Ni
20Pd
30 alloy. On the other hand, fine Ti
2Pd type precipitates were formed upon aging in the Ti
52Ni
18Pd
30 alloy within the aging temperature range of 673-1073 K. The transformation temperature of the Ti
52Ni
18Pd
30 alloy was sensitively dependent on the aging temperature. The Ti
2Pd type nanoscaled precipitates were found to be very effective in enhancing the high temperature dimensional stability during shape memory cycling. Excellent shape memory properties with a large recovery strain and a small plastic strain even at 500 MPa were observed in the Ti
52Ni
18Pd
30 alloy solution treated and aged at lower temperatures of 673 and 773 K owing to the formation of fine and dense Ti
2Pd type precipitates.
View full abstract
-
Mitsuhiro Matsuda, Masatoshi Mitsuhara, Kazuki Takashima, Minoru Nishi ...
2016 Volume 57 Issue 3 Pages
250-256
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: December 04, 2015
JOURNAL
FREE ACCESS
The antiphase boundary (APB)-like structure of B19 martensite in the Ti-Ni-Pd alloy was investigated by means of conventional transmission electron microscopy and high-angle annular dark-field scanning transmission electron microscopy. Some APB-like structures with wide and curved contrast exhibited shifts along the (010)
B19 and (001)
B19 planes; that is, it exhibited facets composed of those planes at the atomic level. This atomic displacement reflects the atomic movement stemming from not only martensitic but also a kind of R-phase transformations.
View full abstract
-
Yoshiyuki Nakata, Yutaka Iizuka, Takafumi Ono
2016 Volume 57 Issue 3 Pages
257-262
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: December 11, 2015
JOURNAL
FREE ACCESS
The fractions of Al atoms at three kinds of crystallographic sites were determined in a Cu-15.5Al-4.0Ni (mass%) alloy before and after aging using powder X-ray analysis in order to clarify the effect of aging on the martensite start temperature,
Ms. The ordering between first nearest neighbors (the B2 ordering) was almost finished even just after quenching, but the ordering between second nearest neighbors (the L2
1 ordering) was incomplete. The B2 type ordering occurs in advance of the L2
1 ordering in Cu-Al-Ni alloys as well as in Cu-Al-Zn alloys. The degree of L2
1 order increases from 0.699 to 0.844 during aging at 200°C for an hour. The increase in
Ms during the aging is attributed to the L2
1 ordering in Cu-Al-Ni alloys.
View full abstract
-
Daichi Minami, Tokuteru Uesugi, Yorinobu Takigawa, Kenji Higashi
2016 Volume 57 Issue 3 Pages
263-268
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: December 11, 2015
JOURNAL
FREE ACCESS
The effect of alloying element X (X = Al, Sn, Zr, Ta) on the transformation strains and phase stabilities of Ti-12.5 at%Nb and Ti-25 at%Nb alloys was investigated. The principle strain, η
2, was calculated as a function of the X concentration. The value of η
2 of Ti-12.5 at%Nb-6.25 at%Zr was larger than that of Ti-12.5 at%Nb-6.25 at%Ta. This is consistent with the experimental results. The difference of solution energy, Δ
Hsolα ” - β, was also calculated. The value of Δ
Hsolα ” - β increased with the addition of Al, Sn, Zr, and Ta to Ti-12.5 at% Nb-6.25 at%X alloys. We found a good linear correlation between the experimental values for the decrease of the martensitic transformation start temperature (
Ms), d
Ms/d
c, and the calculated values of Δ
Hsolα ” - β. The effect of the alloying element on the shape-memory properties of Ti-Nb-based alloys were evaluated from the first-principles calculations.
View full abstract
-
Yuta Kimura, Xiao Xu, Kodai Niitsu, Toshihiro Omori, Ryosuke Kainuma
2016 Volume 57 Issue 3 Pages
269-277
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: January 18, 2016
JOURNAL
FREE ACCESS
In the present study, Ni content dependence of martensitic transformation behavior in Ti
50−xNi
40+xCu
10 alloys (
x = 0.0–3.0) was investigated, and then the superelastic behavior of a
x = 2.4 alloy was examined at low temperatures. The Ti
50−xNi
40+xCu
10 alloys are in B2 single-phase up to
x = 2.4 at 1373 K. The B2/B19 and B19/B19′ transformation temperatures decrease with increasing
x and the lowest martensitic transformation starting temperature of 125 K was detected. In the alloys with Ni compositions over
x = 1.4, a pre-martensitic “intermediate” phase was detected by thermoanalysis measurements. While the middle eigenvalue λ
2 is close to 1.0, which was found to be independent of the Ni content, the thermal hysteresis,
Thys increases with increasing Ni content. This is explained by the drastic decrease in transformation entropy change. Although starting to drastically increase at temperatures below 100 K, the temperature dependence of stress hysteresis in compression testing is basically smaller than that in Ti
48.2Ni
51.8 binary alloy.
View full abstract
-
Takashi Fukuda, Gakudai Yamasaki, Hiroaki Yoshinobu, Tomoyuki Kakeshit ...
2016 Volume 57 Issue 3 Pages
278-282
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
We have studied deformation behavior of two kinds of iron-doped Ti-Ni shape memory alloys under tensile stress applied in the [111] direction. One is Ti-46Ni-4Fe (at%) alloy which transforms to the R-phase and the other is Ti-44Ni-6Fe (at%) alloy which transforms to the commensurate phase (C-phase) in the cooling process. The stress-strain curve measured in the R-phase region shows a residual strain due to rearrangement of variants while that measured in the C-phase shows a pseudoelastic behavior characteristic to stress-induced martensitic transformations. The strain-temperature curve measured under constant stress shows an obvious transformation strain associated with the transformation to the R-phase, while a bend point appears associated with the transformation to the C-phase.
View full abstract
-
Takahiro Sawaguchi, Tadakatsu Maruyama, Hiroaki Otsuka, Atsumichi Kush ...
2016 Volume 57 Issue 3 Pages
283-293
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 15, 2016
JOURNAL
FREE ACCESS
Fe–Mn–Si-based alloys exhibit a shape-memory effect associated with deformation-induced γ → ε martensitic transformation and its reversion. The γ → ε martensitic transformation also enhances mechanical properties, such as strength, hardness, wear-resistance and low-cycle fatigue lives of the alloys. In this article, we review fundamental researches on transformation behavior, microstructural and crystallographic characteristics, and functional and mechanical properties of the Fe–Mn–Si-based alloys, and introduce various examples of their practical applications. A special emphasis is placed on their new application as architectural seismic dampers, which were developed based on a new finding of the passive two-way martensitic transformations under cyclic tensile-compressive loading.
View full abstract
-
Kuo-Hsiung Tseng, Chih-Ju Chou, To-Cheng Liu, Yu-Han Haung, Meng-Yun C ...
2016 Volume 57 Issue 3 Pages
294-301
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
For this study, electrical discharge machining (EDM) and the submerged arc discharge method (SADM) were used to melt a silver-copper composite metal in deionized water through concentrated arc energy in order to produce metal fluids containing nano- and submicron particles. The fabrication process did not require additional chemicals, and was simple and efficient. The critical processing parameters for EDM were the discharge voltage and current as well as the on-off duration for pulse discharge; the sample concentration could be controlled under appropriate conditions. The experimental results revealed that, through electronic system design and manufacturing (ESDM), silver-copper composite metal particles could be achieved at a nano to submicron level. In addition, the results obtained varied according to differences in the on-off duration regarding pulse discharge. In this study, when the discharging parameter (
Ton-
Toff) was at 30 : 50, nanocomposite fluids with an optimal concentration and small particles were obtained. The application of EADM could enable the mass production of composite metal fluids or particles at low cost and high efficiency. Employing EADM for the fabrication of composite metal fluids or particles warrants research attention, and the process itself can be developed further.
View full abstract
-
Do Viet Thang, Nguyen Van Thanh, Nguyen Thi Hien, Nguyen Huy Sinh, Ngu ...
2016 Volume 57 Issue 3 Pages
302-304
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
In order to explore a way to tailor thermal hysteresis behavior of spin-crossover (SCO) complexes, a series of seven Fe
II(LX
2) complexes with different ligand configurations has been designed or reconstructed. These Fe
II(LX
2) complexes differ in axial ligands X = Py, CNPY, NC
5H
4CH
3, NC
5H
4OCH
3, NC
5H
4Cl, X = NC
5H
4Br, and Him. Geometric structure, electronic structure, and magnetic properties of Fe
II(LX
2) complexes have been investigated using density-functional theory with full geometry optimization. Our calculated results show that the spin-state electrostatic-energy difference (Δ
U) of these Fe
II SCO complexes can be tailored by adjusting the p
Ka constant of axial ligands X. The increase of Δ
U of these Fe
II SCO complexes from −12.18 eV to 6.64 eV results from the increase of p
Ka constant of axial ligands X from 1.10 to 7.00. The role of axial ligands X in determining SCO behavior of Fe
II SCO complexes has been revealed. In addition, our previous study (N. A. Tuan: J. Appl. Phys. 111 (2012) 07D101) demonstrated that thermal hysteresis of spin-crossover increased with the Δ
U of Fe
II SCO complexes. These results would give some hints into how thermal hysteresis can be tailored in Fe
II SCO complexes.
View full abstract
-
Takumi Okada, Michael C. Faudree, Naoya Tsuchikura, Yoshitake Nishi
2016 Volume 57 Issue 3 Pages
305-311
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 15, 2016
JOURNAL
FREE ACCESS
Experimental results show applying homogeneous low-energy electron beam irradiation (HLEBI) treatment of 0.30 MGy to both sides of sandwich structural CFRP/ABS/CFRP composite constructed of an ABS core between two thin plies of carbon cross textile fiber/epoxy CFRP apparently increased Charpy impact values,
auc at all fracture probabilities,
Pf at temperatures of 77, 200 and 300 K, within the low temperature range of aircraft operation and below the minimum of reusable launch vehicle operation in space reported as 116 K. At median-
Pf = 0.50
auc was increased 98% from 11.4 to 22.5 kJ m
−2 at low temperature of 77 K, while the HLEBI increased
auc at
Pf = 0.50 221% and 25% at 200 and 300 K, respectively. Although the lowest statistical impact value calculated by the 3-parameter Weibull equation,
as at
Pf = 0 (
as) was reduced in the 200 K samples,
as was improved for the 77 and 300 K samples. The lower
as for the 200 K samples is probably the result of high scatter in the data although the
auc was remarkably improved at all experimental
Pf. In general, the
auc increased with test temperature. Optical observation shows the HLEBI appears to increase the
auc by preventing brittle shattering of the ABS core in the 77 and 200 K samples, and increasing core ductility in the 300 K samples. Within the outer single CFRP plies the HLEBI strengthens by generating dangling bonds in the epoxy matrix as micro-compressive forces increasing adhesion to the fibers by terminated atoms by Coulomb attractive force. Since calculated HLEBI penetration depth,
Dth into the sample was less (119 µm) than the 265 µm CFRP ply thickness, it is possible the strengthened plies carried the load protecting the ABS core. It is also possible the highly conductive carbon fibers transferred charge to the ABS core, generating dangling bonds and/or polarizing the ABS polymer strengthening the ABS itself preventing shattering.
View full abstract
-
Koki Shimosakaida, Shinpei Fujii
2016 Volume 57 Issue 3 Pages
312-315
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 15, 2016
JOURNAL
FREE ACCESS
Recently, new compounds Mn
2RuSn and Mn
2RuSi were synthesized and their crystal structures were studied by X-ray diffraction measurements. This measurement indicates that they have a Heusler-like cubic structure, but the details have been unclear so far. To clarify their atomic arrangement and magnetic order, we carried out first-principles total-energy calculations for several different atomic arrangements, together with ferrimagnetic and ferromagnetic ordering. The comparison among total energies indicates that the most stable structure is a ferrimagnetic Hg
2CuTi one in both Mn
2RuSn and Mn
2RuSi. We also found that the compound Mn
2RuSi with the Hg
2CuTi structure could be a half-metallic ferrimagnet.
View full abstract
-
Kosuke Ozono, Yoshifuru Mitsui, Masahiko Hiroi, Rie Y. Umetsu, Kohki T ...
2016 Volume 57 Issue 3 Pages
316-320
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 15, 2016
JOURNAL
FREE ACCESS
The magnetic and structural properties of ferromagnetic MnCo
0.92Fe
0.08Ge were investigated by magnetization and X-ray powder diffraction measurements in magnetic fields up to 5 T. The compound showed first-order transition between the paramagnetic and ferromagnetic state with a thermal hysteresis of approximately 24 K, which was accompanied by the martensitic transformation from the hexagonal Ni
2In-type structure to the orthorhombic TiNiSi-type structure in the vicinity of 275 K. The cell volume expanded by 4.1% during the martensitic transformation. The magnetic moment of MnCo
0.92Fe
0.08Ge was estimated to be 111 Am
2 kg
−1 (3.7 μ
B/f.u.) at 10 K. The compound showed both metamagnetic transition and magnetic field-induced martensitic transformation.
View full abstract
-
Nobumitsu Shohoji
2016 Volume 57 Issue 3 Pages
321-328
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 05, 2016
JOURNAL
FREE ACCESS
Equilibrium isothermal pressure-composition relationships reported for H solubility in body centered cubic (bcc) V
1−yM
yH
x (M = Cr, Mo, Fe or Co) by Suzuki
et al. recently on this journal were analyzed with statistical thermodynamics under
a priori assumption of constant H-H interatomic interaction energy
E(H-H) within homogeneity composition range of bcc V
1−yM
yH
x phase at arbitrary temperature
T. Results of the present statistical thermodynamic analysis showed that detected H solubility suppression for the examined V
1−yM
yH
x was consistently interpreted in terms of decrease of available number θ for occupation by H atoms per metal atom in the V
1−yM
y lattice from θ = 0.55 determined for bcc VH
x in the earlier work of the author. The extent
Q of stabilization of H atoms in the V
1−yM
y lattice through formation of H-V and H-M bonds was one of principal parameters determined by the statistical thermodynamic analysis. It was intriguing to note that
Q(V
1−yM
yH
x) with M = Fe and Co became less negative than
Q(VH
x) in pure bcc VH
x implying that the extent of stabilization of H atoms in V
1−yM
y lattice with M = Fe or Co increased with reference to that in pure VH
x in spite of decreased θ from that (0.55) in VH
x. On the other hand,
Q(V
1−yM
yH
x) with M = Cr and Mo became less negative (that is decreased stability of H) than
Q(VH
x) corresponding straightforwardly to the detected decrease of θ value from that in VH
x. Noting the promoted H permeability reported for V
1−yFe
y membrane by Suzuki
et al., search for alloying element M that induced H solubility drop form that in the bcc V but with effect of enhancing stability of H in the V
1−yM
y lattice was concluded to be a pragmatic guideline for the screening of alloying constituent towards development of V-based H permeation membrane material.
View full abstract
-
Koji Wada, Kenta Takeshima, Tokuteru Uesugi, Yorinobu Takigawa, Kenji ...
2016 Volume 57 Issue 3 Pages
329-334
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 15, 2016
JOURNAL
FREE ACCESS
In this work, the effects of solute Fe, Zn, and Mg on the suppression of recrystallization in Al are studied. The materials are Al-22.2 atomic parts per million (at ppm) Fe, Al-53.6 at ppm Fe, Al-0.1 at% Mg, Al-1.1 at% Mg, Al-0.1 at% Zn, and Al-3.0 at% Zn. All were synthesized using high-purity starting materials. The amount of impurities other than the additional elements is less than a few ppm. The variation in the Vickers hardness with annealing time after isothermal annealing treatments at various temperatures is measured. The results of the isothermal annealing treatments are discussed in terms of the Johnson–Mehl–Avrami–Kolmogorov (JMAK) equation. The effect of the suppression of recrystallization per concentration unit is highest for Fe, less so for Mg, and least for Zn. The values of the apparent activation energy for recrystallization are calculated as: 139, 146, 63, 66, 47.7, and 67 kJ/mol for Al-22.2 at ppm Fe, Al-53.6 at ppm Fe, Al-0.1 at% Mg, Al-1.1 at% Mg, Al-0.1 at% Zn, and Al-3.0 at% Zn, respectively. The values of the apparent activation energy for recrystallization are close to the values of the activation energy for grain boundary diffusion in the same alloy systems.
View full abstract
-
Xiaolong Dong, Hongwei Zhao, Lin Zhang, Hongbing Cheng, Jing Gao
2016 Volume 57 Issue 3 Pages
335-343
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
Some experimental geometry parameters of four-point bending tests, such as span ratio and support radius, obtained from experience, likely lead systematic errors into the final results. In this paper, some typical geometry effects of four-point bending tests for thin sheet are investigated by employing finite element analysis (FEA). In order to assure the reasonability and accuracy of the FEA results, the standard tensile tests and four-point bending tests are carried out by commercial instruments. Based on the simulation results, it is noted that the stress distribution between the inner supports and outer supports is different with the variation of span ratio. The maximum wedging stress is located near the inner supports. According to the study, the optimum value of the span ratio is suggested to be around 1/3 at plastic stage. In addition, the effects of support radius and contact roughness are also discussed to make a beneficial reference for designing four-point bending experiments and devices.
View full abstract
-
Woei-Shyan Lee, Yu-Chi Huang
2016 Volume 57 Issue 3 Pages
344-350
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 05, 2016
JOURNAL
FREE ACCESS
The mechanical properties and dislocation substructure of 6061-T6 aluminum alloy deformed at temperatures of 0°C, −100°C and −196°C and strain rates of 1000 s
−1, 3000 s
−1 and 5000 s
−1 are investigated using a compressive split-Hopkinson pressure bar. It is found that the flow stress and strain rate sensitivity increase with increasing strain rate, but decrease with increasing temperature. In addition, the work hardening rate decreases with increasing strain rate and temperature. The flow stress corresponding to a true strain of 0.6 is modelled using a power law expression with an activation energy of 1.7 kJ/mol and an average strain rate sensitivity of 0.154. The dislocation density increases with increasing strain rate and decreasing temperature, and leads to a greater flow stress. A greater multiplication and tangling of the dislocations occurs at higher strain rates and lower temperatures. The flow stress and square root of the dislocation density are linearly related via the Bailey-Hirsch type relation σ = σ
0 + α
1Gb√ρ , where α
1 has a value of 0.46 for the current 6061-T6 aluminum alloy.
View full abstract
-
Shih-Hang Chang, Chen Chien, Shyi-Kaan Wu
2016 Volume 57 Issue 3 Pages
351-356
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
Ti
50Ni
50−xFe
x shape memory alloys (SMAs) have higher inherent and intrinsic internal friction peaks during R → B19′ transformation ((
IFPT +
IFI)
R→19′) than during B2 → R transformation ((
IFPT +
IFI)
B2→R). The reasons are that the former has the larger transformation strain and the abundant movable twin boundaries appearing in both R-phase and transformed B19′ martensite. Ti
50Ni
50−xFe
x SMAs also exhibit higher (
IFPT +
IFI)
R→19′ peaks than annealed Ti
50Ni
50 SMA after cold-rolling because the latter needs dislocations to be introduced to form R-phase, but the former does not. For Ti
50Ni
48Fe
2 SMA, the tan δ values of the (
IFPT +
IFI)
B2→R and (
IFPT +
IFI)
R→B19′ peaks and that of
IFI in the R-phase regime decrease after the dehydrogenation treatment at 600°C for 6 h in a vacuum furnace, due to pinning of the twin boundaries by hydrogen atoms. However, the hydrogen pinning effect is small for
IFI in B2 phase and B19′ martensite. Ti
50Ni
50−xFe
x SMAs with
x = 2 and 3 at% have quite good (
IFPT +
IFI)
R→19′ tan δ values (> 0.035), but their low transformation temperatures may restrict their use in practical high-damping applications.
View full abstract
-
Akihiro Yoshimura, Yasunari Matsuno
2016 Volume 57 Issue 3 Pages
357-361
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
A novel method for the production of gold micrometer-sized particles from secondary sources is presented. The method consists of the leaching of gold using dimethyl sulfoxide (DMSO, (CH
3)
2SO) solutions containing copper chloride (CuCl
2) followed by the precipitation of gold with hydrochloric acid (HCl). Gold was dissolved in a DMSO solution with 0.1–0.2 M CuCl
2 and 0–0.3 M sodium chloride (NaCl) at 343 K. The precipitation of dissolved gold was performed by the addition of HCl, during which the effects of the concentration of the Cl
− ion was investigated. It was found that the initial gold dissolution rate in DMSO solutions with CuCl
2 was up to 14.8 mg cm
−2 h
−1, which was larger than the rates obtained with other leaching methods, but smaller than the author’s previous research using copper bromide (CuBr
2) and potassium bromide (KBr). A gold recovery efficiency of up to 92.6% was obtained by precipitation with HCl solution. We obtained “raspberry-like” or “confeito-like” gold microspheres under the condition of less than 1.5 M of Cl
− ion and over 0.013 M of dissolved gold. Our results demonstrated that a circulating system for gold leaching and recovery and production of functional material could be developed, which would offer a number of advantages, including eco-friendliness, easy operation, low costs, and minimization of chemical sludge production.
View full abstract
-
Toshiaki Toyoda, Yuji Sutou, Shoko Komiyama, Daisuke Ando, Junichi Koi ...
2016 Volume 57 Issue 3 Pages
362-367
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
The hardness and wear properties of Ti-Mo-C-N films were investigated by nanoindentation and ball-on-disc measurements, respectively. Ti-Mo-C-N films were deposited onto a stainless steel substrate by a reactive RF magnetron sputtering in the mixture of argon (7.5 ccm) and nitrogen (0–6.0 ccm) gases using Ti
25Mo
25C
50 target. Ti-Mo-C film deposited without nitrogen gas flow showed a hardness of 34.8 GPa. The hardness drastically decreased with increasing nitrogen gas flow rate (
fN2) and reached to a minimum hardness of 16.4 GPa at
fN2 = 2.0 ccm. Contrarily, at over
fN2 = 3.0 ccm, the hardness drastically increased with increasing
fN2 and reached a maximal value of 32 GPa, and then slightly decreased again with further increase of
fN2. It was found by TEM observation that the drastic decrease in hardness is caused by the formation of nanocrystalline microstructure, while the increase in hardness is due to the microstructural change from nanocrystalline to columnar structure. The friction coefficient decreased with increasing
fN2 and the film deposited at
fN2 = 5.0 ccm showed a minimum value of 0.27. The simple oxidation test in air indicated that lubricious MoO
3 is easy to be formed in the film deposited at a high
fN2, which should cause the reduction of friction coefficient.
View full abstract
-
Arata Yagi, Chisato Kubo, Masae Kanda, Itaru Jimbo, Yoshitake Nishi
2016 Volume 57 Issue 3 Pages
368-372
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 15, 2016
JOURNAL
FREE ACCESS
2-layer Titanium/Polyurethane (Ti/PU) laminated sheets were prepared by a new adhesion method, a double-step treatment consisting of applying low dose (≦ 0.43 MGy) homogeneous low energy electron beam irradiation (HLEBI) prior to hot-press under 5 MPa and 413 K. Although the weak hot-press adhesion of the Ti/PU was observed without HLEBI, the new adhesion raised the bonding forces as evidenced by the mean adhesive forces of peeling resistance (
oFp). Based on the 3-parameter Weibull equation, the lowest
oFp value at peeling probability (
Pp) of zero (
Fs) could be estimated. An increasing trend in
Fs occurred by the double-step treatment applying HLEBI up to 0.22 MGy reaching a maximum at 123 Nm
−1, improving the safety level without radiation damage. XPS (X-Ray Photoelectron Spectroscopy) observations of the peeled 0.22 MGy irradiated Ti revealed generation of a TiO
2 peak at 530.6 eV possibly explaining the increased adhesion. The residual PU deposition is apparently found to be retained on the Ti sheet by inter-matrix fracture of PU further into the thickness. This can be explained by the adhesion force between Ti/PU being stronger than the cohesive force of PU polymer itself.
View full abstract
-
Chisato Kubo, Masae Kanda, Olivier Lame, Jean-Yves Cavaille, Yoshitake ...
2016 Volume 57 Issue 3 Pages
373-378
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
2-layer laminated sheets (PE/18-8) with Polyethylene (PE) and austenitic 18-8 stainless steels (18-8) were prepared by a new adhesion method, a double-step treatment consisting of applying low dose (≦0.43 MGy) homogeneous low energy electron beam irradiation (HLEBI) prior to hot-press under 5 MPa and 343 K. Although the weak hot-press adhesion of the PE/18-8 was observed without HLEBI, the new adhesion raised the bonding forces as evidenced by the mean adhesive forces of peeling resistance (
oFp). Based on the 3-parameter Weibull equation, the lowest
oFp value at peeling probability (
Pp) of zero (
Fs) could be estimated. An increasing trend in
Fs occurred by the double-step treatment applying HLEBI up to 0.30 MGy reaching a maximum at 0.85 N m
−1, improving the safety level without radiation damage. When HLEBI cut the chemical bonds in PE polymer and generated terminated atoms with dangling bonds, they probably induced the chemical bonding. Therefore, increasing adhesion force between the laminated sheets could be explained.
View full abstract
-
Naoto Shiraki, Yuki Usui, Toshitake Kanno
2016 Volume 57 Issue 3 Pages
379-384
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
The purpose of this study is to investigate the effects of number of graphite nodules on fatigue limit and fracture origins in spheroidal graphite cast iron where carbon content and the number of graphite nodules are changed. As specimens, spheroidal graphite cast irons with 3.0, 3.2, 3.4, 3.6 and 3.8 mass% carbon content were produced respectively. Matrix was conducted pearlite (PDI) and ausferrite (ADI) by heat treatment (normalizing and austempering). The mean diameter of the graphite nodule decreases as the carbon content increases, and the number of graphite nodules per unit area increases. No differences were observed in tensile strength as a result of variations in the number of graphite nodules. The rotating bending fatigue test was conformed to JIS (Japanese Industrial Standards). Load frequency was 47 rpm, number of cycle to discontinue test was 1.0 × 10
7 cycles, and the specimen used was the 1 type of 8.00 mm in diameter. All the fracture surfaces were observed with a scanning electron microscope. The relationship between the characteristics of fatigue strength and the size of fracture origins (defect size) was investigated.
No differences were observed in fatigue limit as a result of variations in the number of graphite nodules. Fracture origins were micro-shrinkage, unspheroidizing graphite nodule and aggregate graphite nodules. The percentage of fracture origin of aggregate graphite nodules was increased by cluster of the graphite nodules. The reason of this phenomenon was due to the decrease of the graphite nodules spacing. The mean defect size in each sample was constant irrespective of the change of number of graphite nodules, which was good agreement with the results of the fatigue limit.
View full abstract
-
Kang-Il Lee, Kazuto Sato, Kazuhiro Ogawa
2016 Volume 57 Issue 3 Pages
385-391
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
The properties of agglomerated and sintered powders of the cermet of yttria-stabilized zirconia (YSZ)/CoNiCrAlY and coatings thereof were investigated. Three multimodal cermet powders were prepared with different compositions (75% CoNiCrAlY:25% YSZ; 50% CoNiCrAlY:50% YSZ; and 25% CoNiCrAlY:75% YSZ) for deposition by a cold-spraying process. Each of the cermet powders was successfully deposited onto a bond-coated substrate by the cold-spray process with low kinetic energy. Each feedstock powder ensured a homogeneous distribution of YSZ powders in the coating layer. The microstructural characterization and phase analysis of the feedstock powders and the as-sprayed coatings were obtained by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray spectroscopy (EDX). In the XRD and EDX results, the YSZ content in the coating increased with the increase of YSZ content in the powder blend. Against conventional expectations, the deposition efficiency and hardness of the as-sprayed coatings were improved by low gas pressure. In particular, the as-sprayed coatings with more than 50 mass% YSZ showed decreased cracks in the coating layer. To understand these results, the cermet particles were coated onto Al substrates by cold-spraying. Then, the particles were cut open to observe the bonded cross-sectional surface by focused ion beam (FIB) analysis.
View full abstract
-
Mayur Shukla, Sumana Ghosh, Nandadulal Dandapat, Ashis K. Mandal, Vams ...
2016 Volume 57 Issue 3 Pages
392-396
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
Microwave-assisted reactive brazing technique was utilized for joining of alumina ceramics at 950°C and 1050°C for 20 min in argon atmosphere using TICUSIL (68.8Ag-26.7Cu–4.5Ti in mass%) paste as the braze alloy. Conventional heating technique was also employed for comparison purpose only. The microwave and conventionally brazed joints were characterized by X-ray diffraction, scanning electron microscopy, energy dispersive X-ray analysis and Vickers microhardness measurement. X-ray diffraction data showed that the Ti-based compounds were formed at the substrate-filler alloy interfaces of the microwave and conventionally brazed joints. Scanning electron microscopy exhibited the formation of thicker reaction region in the case of joints microwave brazed at higher temperature. Energy dispersive X-ray analysis determined the elemental compositions across the joint cross-section. Vickers microhardness measurements indicated more reliable performance of the joints microwave brazed at lower temperature. Hermiticity of the microwave and conventionally brazed joints was evaluated by Helium leak test and found to be acceptable for actual applications.
View full abstract
-
Toshihiro Yamamoto, Takashi Furukawa, Hideo Nishino
2016 Volume 57 Issue 3 Pages
397-403
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: January 18, 2016
JOURNAL
FREE ACCESS
Guided wave testing offers an efficient screening method for thinning of pipe walls because of its long inspection range and its ability to inspect pipes with limited access. However, the existence of an elbow in pipes makes the interpretation of echo signals difficult. The present study investigates the sensitivity of defect detection when guided wave testing is applied to detect a defect at a pipe elbow. To examine the defect sensitivity when a defect exists at different locations on an elbow, an artificial defect was produced at one of 12 different locations on the outer surface of the elbow of each aluminum alloy piping specimen. The defect signals were observed as the defect depth was gradually increased at each defect location to obtain the defect sensitivity. The transmitted guided wave frequency was in turn set to 30 kHz, 40 kHz, and 50 kHz. At 30 kHz, high sensitivity values were obtained at the intrados of the elbows, whereas at 40 kHz and 50 kHz, high sensitivity values were obtained at their extrados. This paper also shows the results of computer simulations that used the same configuration as that used in the experiments to analyze the propagation behavior of guided waves passing through the elbow. In addition to the experimental results, the simulation results indicate that the defect-sensitive locations are controlled by the guided wave frequency. Thus, proper selection of the excitation frequency for guided wave testing enables efficient defect detection at pipe elbows.
View full abstract
-
Thet Thet Cho, Sumio Sugiyama, Jun Yanagimoto
2016 Volume 57 Issue 3 Pages
404-409
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 05, 2016
JOURNAL
FREE ACCESS
Although the recycling of aluminium has many environmental and economic benefits, the accumulation of impurities is a problem in the case of repeated recycling. In this study, the purification of A7075 wrought aluminium alloy and ADC12 based hypereutectic aluminium alloy was conducted by the backward extrusion process under a semisolid condition. The effect of process parameters such as the semisolid temperature and backward extrusion ratio was investigated. From the results of optical microscopic imaging, scanning electron microscopy (SEM) and energy-dispersive X-Ray spectroscopy (EDS) analysis, it was confirmed that the percentage of purified aluminium, the distribution of aluminium and the yield of the purified part for A7075 alloy were significantly affected by the semisolid temperature and extrusion ratio. For ADC12 based hypereutectic aluminium alloy, it was found that the silicon flakes still remained even in the unextruded part after the purification process.
View full abstract
-
Byung Keun Kang, Chun Pyo Hong, Young Soo Jang, Byoung Hee Choi, Il So ...
2016 Volume 57 Issue 3 Pages
410-416
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
The effect of casting parameters on the microstructure and mechanical properties during semisolid die casting using commercial ADC10 alloys was studied. Fine and uniform globular microstructures were produced using optimized casting conditions, where low pouring temperatures of 878 K (605°C) and pre-heating of the slurry-making container temperatures up to 523 K (250°C) resulted in better microstructural control. To obtain the conditions for high quality slurries within a mass production system, the microstructural characteristics of slurries produced with various cooling rates were analyzed. Cooling rates between 0.1°C/s and 0.9°C/s were found to result in comparatively good microstructural characteristics, which corresponded to form factors of 0.75 or greater and α-Al particles less than 65 µm in the slurries. The hardness and tensile strength were evaluated for T6 heat-treated semisolid die cast products and compared with the properties of high-pressure die cast specimens. Transmission electron microcopy (TEM) and electron probe micro-analysis (EMPA) were also used to identify and verify the precipitated secondary phases and the solute distribution.
View full abstract
-
Ryo Nomura, Masae Kanda, Michael C. Faudree, Itaru Jimbo, Yoshitake Ni ...
2016 Volume 57 Issue 3 Pages
417-422
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 05, 2016
JOURNAL
FREE ACCESS
A new process of internal activation of glass fiber reinforced thermoplastic polymer (GFRTP) of Polypropylene (PP) was achieved by homogeneous low energy electron beam irradiation (HLEBI) to the interlayered glass fiber chopped strand mats (GF-CSM) prior to assembly. Panels were fabricated by hot-press consisting of 5 HELBI-treated GF-CSMs between 6 untreated PP sheets. HLEBI improved the Charpy impact value (
auc) of the internally activated GFRTP. HLEBI from 0.22 to 0.86 MGy mostly improved the
auc at each accumulative probability of fracture (
Pf). Based on the 3-parameter Weibull equation, the
auc value was defined as the statistically lowest impact value,
as estimated as the
auc at
Pf = zero. The highest
as values at more than 87 kJ/m
2 were found for GFRTP irradiated at 0.65 MGy which appears to be at or near the optimum HLEBI dose. Strengthening the adhesion force at the extremely broad surface area of the fibers increased interfacial friction force to prevent fiber pull out, fiber/matrix debonding and crack generation in the hard to adhere PP matrix GFRTP, resulting in increasing
auc of GFRTP with glass fiber surface-activated by HLEBI.
View full abstract
-
S. Morimoto, H. Yukawa, T. Nambu, Y. Murata
2016 Volume 57 Issue 3 Pages
423-427
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
The possibility of a new ammonia synthesis process has been investigated by utilizing V-based alloy membrane under moderate temperature and pressure conditions. Three membrane samples with different coating conditions of Pd-Ag alloy on the outlet side surface have been tested. It is found that the deposition of Pd-Ag alloy on the outlet side surface is needed for V-based alloy membrane for hydrogen permeation at 623 K. While keeping the hydrogen permeation condition, nitrogen gas is flowed to the outlet side surface of the membrane samples, and the reaction gas is bubbled into distilled water to detect ammonia formation by using Nessler’s reagent. Ammonia is not synthesized for the membrane sample coated thickly with Pd-Ag alloy on the outlet side surface, indicating that Pd-Ag alloy does not have a dissociation ability of nitrogen molecule. In contrast, ammonia is formed for the membrane sample coated in a grid pattern with Pd-Ag alloy on the outlet side surface. In this case, both V-based alloy and Pd-Ag alloy coexist on the outlet surface, and hydrogen atoms permeating through the membrane and nitrogen atoms dissociated on the surface of V-based alloy probably react with each other to form ammonia.
View full abstract
-
Takashi Danjo, Satoru Kawasaki
2016 Volume 57 Issue 3 Pages
428-437
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: January 22, 2016
JOURNAL
FREE ACCESS
To develop an alternative ground improvement technique in coastal areas based on bio-stimulation, we investigated sand cementation using bacteria that have been shown to enhance beachrock formation. We conducted cementation tests using
Pararhodobacter sp. strain SO1, a local ureolytic bacteria originating from the sand near beachrock in Okinawa, Japan. Specifically, we attempted to cement sand specimens to unconfined compressive strength (UCS) of several MPa and establish the influence of several test conditions (curing temperature, injection interval of cementation solution, Ca
2+ concentration and sodium malate concentration in the cementation solution, and test period) on the UCS. Column specimens were cemented up to UCS of 10 MPa after 28 days under the conditions (curing temperature; 30°C, injection interval; 1 day, Ca
2+ concentrations in cementation solution; 0.3 M). Multiple regression analysis showed that the relevant conditions for UCS were test period,
D (days), and Ca
2+ concentration of the cementation solution,
Cca (M). The prediction formula for UCS,
qud (MPa), was experimentally determined to be
qud = 48.3
Cca + 0.456
D − 19.51. Overall, the results of this study will contribute to the application of a new technique for coastal sand improvement and bio-stimulation.
View full abstract
-
Takao Ueda, Tatsuya Oki, Shigeki Koyanaka
2016 Volume 57 Issue 3 Pages
438-444
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
Stereological correction, which corrects an overestimation of the degree of liberation of minerals in a two-dimensional measurement, has not been adequately established, despite its importance in the evaluation of not only the crushed product but also the efficiency of comminution and sorting in the mining process. A unique numerical method was conducted using Discrete Element Method in order to investigate the relationship between the two-dimensional information obtained by cross-sectional measurement and three-dimensional practical information. First, spherical particles of a certain-sized dispersion were packed in a sampling cell. Following this, phases with a lognormally distributed volume fraction, which was designated by a median
MD and standard deviation
SD, were placed between the particles. Finally, the serial cross-sectional information was analyzed in the height direction, and the following fundamental results were obtained: 1) the area fraction of the cross-sectional circles distributed around the practical volumetric fraction and 2) the degree of liberation was overestimated by the two-dimensional cross-sectional measurement. A series of parametric studies was then conducted on the phases using various
MD and
SD values, and a correlation between the two-dimensionally measured and three-dimensional actual parameters was obtained. In using this correlation, the volumetric distribution of the phase, together with its degree of liberation (which is usually difficult to measure directly), was estimated with parameters obtained by cross-sectional measurement, such as optical microscopy, QEM*SEM, and MLA. This was based on the assumption that all the particles include a single spherical phase with a lognormally distributed volume.
View full abstract
-
Assayidatul Laila, Makoto Nanko, Masatoshi Takeda
2016 Volume 57 Issue 3 Pages
445-451
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: January 29, 2016
JOURNAL
FREE ACCESS
In this work, the thermoelectric properties of p- and n-type β-FeSi
2, prepared utilizing cast iron scrap chips, have been characterized by measuring the Seebeck coefficient, electrical conductivity and thermal conductivity at temperatures ranging from room temperatures to 800°C. In a previous study, the upgrade recycling of cast iron scrap chips into β-FeSi
2 thermoelectric materials was proposed as an eco-friendly and cost-effective production process. By doping with different substitution concentrations of Co, Mn and Al, the conduction type and properties of β-FeSi
2 can be modified and improved using cast iron scrap chips as a starting material. The effects of the doping elements are discussed for preparing β-FeSi
2 utilizing cast iron scrap chips. Cast iron scrap chips could be preferable as a starting material to replace pure Fe for n- and p-type β-FeSi
2 thermoelectric materials. An optimum composition for n-type β-FeSi
2 0.94C.I.-0.06Co-1.86Si shows that the largest
ZT value of 0.22 occurs at 700°C, whereas for p-type β-FeSi
2 0.92C.I.-0.08Mn-1.86Si, the largest
ZT value of 0.17 occurs at 800°C.
View full abstract
-
Dominik Brkic, Dragutin Nedeljkovic, Lana Putic, Jasna Stajic-Trosic, ...
2016 Volume 57 Issue 3 Pages
452-456
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 05, 2016
JOURNAL
FREE ACCESS
The natural balance in the Earth’s atmosphere is significantly influenced by the human emission of the combustion products, mainly carbon dioxide. Therefore, strong efforts are directed in the direction of the reduction of that emission. The solution might be searched in the direction of the construction of the membrane that would be highly transparent to the carbon dioxide, but not transparent to the other gases commonly present in the waste gases (oxygen, nitrogen, hydrogen, methane). One of the feasible designs for this purpose is dense, non-porous membranes, with zeolite particles dispersed in the polymer matrix. Zeolite particles should increase the solubility of the carbon dioxide, and thus enhance its permeability. In this paper, the possibility of application of polyether-b-amide (with 60% of PEG) as a polymer matrix was tested. For the inorganic component, four different zeolite types with three different pore geometries were tested. The influence of the additive which was added in order to provide good contact between the highly polar and charged zeolite inorganic particle, and hydrophobic polymer chains was also tested.
View full abstract
-
Shinji Isogami
2016 Volume 57 Issue 3 Pages
457-460
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
An optimized homopolar magnetizing fixture consisting of four magnetic pole pieces was developed with the aim of achieving a focused magnetic flux on the surfaces of Nd-Fe-B alloy-based permanent magnets, and thus enhancing the magnetic flux density. In this fixture, only the transverse pieces involved coils providing the same magnetic poles in response to a pulsed current. Rectangular anisotropic and isotropic bonded magnets as well as sintered magnets, having dimensions of 6 mm × 12 mm × 24 mm or 6 mm × 12 mm × 16 mm, were magnetized to multipoles using a prototype fixture in conjunction with a pulsed power source. As a result, the magnetic flux density perpendicular to the surface (
Bz) was increased by 52% relative to that of conventional simple magnets containing the same volume of magnetic compound, with the front and back surfaces magnetized to opposite polarities. In addition, the
Bz polarities of both the front and back sides of the magnet were determined to correspond to N-poles. The distribution pattern of
Bz led us to conclude that the enhanced
Bz and the equal polarity on both sides can both be attributed to the cusp field resulting from the flux generated by the transverse coils of the magnetizing fixture.
View full abstract
-
Canxu Zhou, F. P. Zeng, Bin Liu, Yong Liu, Kun Zhao, Jinzhong Lu, Cong ...
2016 Volume 57 Issue 3 Pages
461-465
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
Advance online publication: February 05, 2016
JOURNAL
FREE ACCESS
The effects of Si addition on microstructures, high temperature compressive properties and creep properties of the β-stabilized Ti-45Al-3Fe-2Mo alloy have been studied in this work. The results show that the Si addition decreases the volume fraction of β phase and precipitates particulate Ti
5Si
3 phase. At the same time, the Si addition improves the high temperature strength of the Ti-45Al-3Fe-2Mo alloy for about 200 MPa at 800°C and decreases the creep strain for about 35% at 800°C under an applied stress of 150 MPa. The decrease in volume fraction of β phase and precipitation of Ti
5Si
3 particles are believed to be the dominant mechanisms for the improvement of the high temperature properties of the Si-doped TiAl alloy.
View full abstract
-
Sang-Min Lee, Jeong-Won Yoon, Seung-Boo Jung
2016 Volume 57 Issue 3 Pages
466-471
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
Board-level drop reliability testing under JEDEC (Joint Electron Device Engineering Council) drop conditions was conducted for low-temperature Sn-58 mass%Bi solder joints. The effects of surface finish and the number of reflow processes (one, three, or five) on the drop reliability of the Sn-58Bi joints were evaluated. Three types of surface finishes were used including electroless nickel immersion gold (ENIG), electroless nickel electroless palladium immersion gold (ENEPIG), and organic solderability preservatives (OSP). We successfully fabricated six types of drop test specimens with various surface finishes and bonding materials, and then performed the board-level drop tests. The board-level drop reliability was improved when using the composite Sn-58Bi solder with epoxy as compared to Sn-58Bi solder without epoxy. In addition, the reliability of the Sn-58Bi epoxy solder/OSP joint was better than both the ENIG and ENEPIG surface finishes. When the number of reflow processes increased, the drop reliability showed two different behaviors; specifically, the reliability of the ENIG and ENEPIG surface finishes decreased while the OSP surface finish improved. The existence of epoxy in the solder paste improved the drop reliability of the solder joints. After drop testing, cracks propagated differently with different surface finishes, namely between Ni
3Sn
4 IMCs and the Ni-P layer for the ENIG surface finish, between Ni
3Sn
4 IMCs and the solder bulk for the ENEPIG surface finish, and within the solder bulk for the OSP surface finish. These data show that, when it is necessary to perform repeated reflow processes for electronic components, solder joints with an OSP surface finish provide better drop test reliability results.
View full abstract
-
Orkun Onal, Berkay Gumus, Bekir Aksoy, Gregory Gerstein, Burhanettin E ...
2016 Volume 57 Issue 3 Pages
472-475
Published: March 01, 2016
Released on J-STAGE: February 25, 2016
JOURNAL
FREE ACCESS
Fatigue performance of micro-scale pseudoelastic nickel-titanium (NiTi) wires was investigated under cyclic bending loading. The current findings demonstrated that the change from macroscopic to microscopic scale promotes the formation of the B19′ phase and significantly hinders stabilization of the R-phase.
View full abstract