巻号一覧
25 巻 (1999)
- 6 号 p. 211-
- 5 号 p. 171-
- 4 号 p. 131-
- 3 号 p. 87-
- 2 号 p. 45-
- 1 号 p. 1-
25 巻, 6 号
選択された号の論文の5件中1～5を表示しています
- |<
- <
- 1
- >
- >|
-
田草川 照彦1999 年 25 巻 6 号 p. 211-218
発行日: 1999/11/15
公開日: 2009/08/11
ジャーナル フリーPDF形式でダウンロード (5006K) -
諏訪 浩史, 高橋 淳, 剱持 潔1999 年 25 巻 6 号 p. 219-224
発行日: 1999/11/15
公開日: 2009/08/11
ジャーナル フリーThe composite materials were made from multi-layer fabrics which were woven with pitch-based carbon fiber rovings and epoxy resin matrix. The relationship between the structure of multi-layer fabrics and interlaminar strength properties of the composites was investigated by executing compression after impact (CAI) test, and compared with those of laminated fabric composites. The results are summarized as follows; From the impact test, it was found that the multi-layer fabrics composites had higher rigidity than that of laminated ones. It was clearly shown from damage area of the composites that the multi-layer fabric composites were the materials with higher resistance to delamination than laminated ones. The proportion of the damage area of multi-layer fabric composites to that of laminated ones was 0.6 to 1. Consequently, CAI strength of the multi-layer fabric composites was about 20% higher than that of laminated ones.抄録全体を表示PDF形式でダウンロード (4194K) -
高田 真之, 辛 純基, 松原 秀彰, 柳田 博明1999 年 25 巻 6 号 p. 225-230
発行日: 1999/11/15
公開日: 2009/08/11
ジャーナル フリーCarbon powders (CP) and carbon fiber (CF) were introduced into glass fiber reinforced plastics (GFRP) composites to obtain fracture detection function. The specimens were evaluated through the relation between a load-displacement curve and an electrical resistance change curve in three point bending test. CP containing GFRP (CPGFRP) has a sensitivity of electrical resistance change at much lower load level than CF containing GFRP (CPGFRP). In loading/unloading tests, CPGFRP showed a large amount of residual electrical resistance which enables the estimation of loading hysteresis.抄録全体を表示PDF形式でダウンロード (6049K) -
足立 廣正, 長谷川 照夫1999 年 25 巻 6 号 p. 231-235
発行日: 1999/11/15
公開日: 2009/08/11
ジャーナル フリーPDF形式でダウンロード (611K) -
自動車用途でのCFRP:現在そして将来魚谷 眞一郎, 柳澤 正良, 伊藤 京一1999 年 25 巻 6 号 p. 236-239
発行日: 1999/11/15
公開日: 2009/08/11
ジャーナル フリーPDF形式でダウンロード (3375K)
- |<
- <
- 1
- >
- >|