The corrosion of cast iron by SO
2 gas at high temperatures was examined. And the following results were obtained :
(1) The corrosion product of cast iron was composed of pyrrhotite Fe
1-xS, wüstite FeO and magnetite Fe
3O
4. In the outer layer, C and P did not diffuse, on the contrary Mn diffused freely and Si did a little.
(2) The corrosion rate was controlled by the parabolic rate law.
(3) Between the corrosion rate and temperature, the exponential law was found.
(4) C promoted the corrosion rate of cast iron, on the contrary Mn did not and Si affected it very little.