Quantitative analysis is made on samples of molten steel, products, scraps and specimens for investigation to rationalize the work of analysis by quantorecorder with the following results.
1.In low voltage spark excitation, Mn 2775.654Å line when Mn content is above 0.1%and Ni 2775.327Å line when Ni content is above 0.8% interfere with Mo 2775.400Å line.Correction to compensate for the errors caused by this interference becomes necessary.
2.Al used as a deoxidizer is apt to affect the analytical values of Si, Mn, Ni, Cu, Mo and V contents.Therefore, the period in which Al killing is necessary should be avoided for sampling, or else the amount of Al used for killing should be kept below 0.3%.
3.Standard samples of high carbon steel (carbon content>1.0%) for analyses of Si and Mn are better to be chosen from actual products.