  • [in Japanese]
    1979 Volume 65 Issue 14 Pages 1983-1984
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Download PDF (2252K)
  • Kazumi OGINO, Atsushi NISHIWAKI
    1979 Volume 65 Issue 14 Pages 1985-1994
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    The X-ray fluoroscopy technique has been successfully applied in studying the CO bubble evolution accompanied with the reduction of silica in blast furnace type slag by carbon-saturated iron in graphite crucible. Visual images have been obtained of the residence and behaviour of the bubbles at slag/metal and slag/graphite interface.
    The main results obtained are as follows:
    (1) The rate of bubble evolution at each interface varies with temperature and slag composition.
    (2) The bubble evolution at slag/graphite interface proceeds more slowly than that at slag/metal interface and is accelerated when slag wets the interface. The shapes of detaching bubbles from the interface are spherical and their diameters are not more than 3 mm.
    (3) The aspect of bubble evolution at slag/metal interface differs greatly with a period of the reaction. In the initial stage, numerous small bubbles evolve vigorously all over the interface, while in the later stage, large bubbles of dome shape are formed periodically at certain sites of the interface.
    (4) The volume of detaching bubble from the interface in stationary state is nearly equal to that calculated from the balance between buoyancy and interfacial tension force.
    Download PDF (11502K)
  • Kazumi OGINO, Atsushi NISHIWAKI, Takahisa SUZUKI, Susumi IKUSHIMA
    1979 Volume 65 Issue 14 Pages 1995-2004
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    The evolution rate of CO gas produced by the reduction of silica in CaO-SiO2-Al2O3 slag by molten carbon-saturated iron in graphite crucible has been measured in the temperature range between 1 510°C and 1 620°C, and the effects of tempenature, slag composition, silicon content of iron and ratio of interface area of slag/metal and slag/graphite on the rate have been examined.
    The rate of CO evolution is proportional to activity of silica in slag and increases with an increase of the interface area. Apparent activation energies of the rate are 87 kcal/mol for acid slag and 62 kcal/mol for basic slag.
    On the basis of the changes of over-all reaction rate with the ratio of the interface areas, the CO evolution rates of unit interface area are evaluated. The proportion of contribution of the reaction at each interface to over-all evolution rate is varied with temperature and slag composition. The rates of silica reduction estimated by present results are in good agreement with that already reported by many investigators.
    The results obtained in this work show a good correspondence to the results of our previous study in which CO bubbles formation were observed by X-ray fluoroscopy method.
    It is suggested that in this experimental condition, the reaction is controlled by chemical reaction step.
    Download PDF (1954K)
  • Takatsu SUGISAKI, Susumu OHTA, Takeshi KITAGAWA, Shunsaku SHIMADA
    1979 Volume 65 Issue 14 Pages 2005-2011
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    On the consideration about the optimum number of tuyeres of blast furnace, the race way depth in comparison with the hearth diameter is noted.
    As the measure of active race way depth in general, “the active race way dimension rate” (η) is adapted to the analysis of relations between practical data.
    In the cases of good operation results of blast furnaces, the values are in the range from 0.45 to 0.50. Therefore, the equations for determining the optimum number of tuyeres are derived by taking η=0.47.
    By taking the generalized combined blast condition into consideration, the constant term in LEONIDOV'S formula is analyzed to get a more optimum answer. Also, the validity of this equation is proved by the data from the blast furnace in operation.
    Download PDF (1183K)
  • Kazumi OGINO, Shigeta HARA, Takashi MIWA, Shinji KIMOTO
    1979 Volume 65 Issue 14 Pages 2012-2021
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    The interfacial tension between molten steel and slag was measured by the sessile drop method with transmission X-ray technique. The results were summarised as follows;
    (1) The increase of oxygen content in steel caused the remarkable decrease of the surface tension of steel and the interfacial tension at steel-slag boundary. The fact shows that the oxygen dissolved in steel acts as the surface-active reagent at metal-slag boundary as well as at metal-gas interface.
    (2) Consequently, the interfacial tension depended in most part on the oxygen content in steel and the effect of slag composition on the interfacial tension was not so much.
    (3) In order to clear the effect of slag composition on the interfacial tension, the experimental results were discussed by the values of Δσ (=σmms) which indicated the differences between the surface tension and the interfacial tension at constant of oxygen content in metal. The values of Δσ dereased with increase of silica content in a slag.
    (4) The work of adhesion between molten steel and slag Wad (=σmsms) was dependent sufficiently on the slag composition. The work of adhesion for a fluoride slag-steel system was smaller than that for an oxide slag-steel system, while the work of adhesion for oxide slag-metal system decreased with increasing of silica content in a slag.
    Download PDF (3502K)
  • Katsuo KINOSHITA, Toshihiko EMI, Manabu KASAI
    1979 Volume 65 Issue 14 Pages 2022-2031
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Temperature- and Stress-field in solidifying shell, and air gap formation in continuous casting mold have been numerically investigated by using a mathematical model to find conditions for strand-casting defect-free slabs. The model is based on a two dimensional non-steady state heat transfer analysis connected with a two dimensional thermal elasto-plastic stress analysis, and is capable of including the interaction between the temperature- and the stress-field. The model also involves operating variables, such as slab size, withdrawal rate, casting temperature, rate of water cooling in mold, mold taper, and, in particular, characteristics of mold flux.
    Calculated variation of heat flux along the mold height agrees well with experimental one. Also, calculated shell profile, which exhibits retarded solidification owing to the formation of air gap near the corner of the shell, closely resembles experimental one.
    The model developed in the present work has enabled us to get comprehensive information on the mode of solidification in continuous casting mold under varying casting conditions without making elaborating experiments. The model has been utilized as a potential simulator to determine optimum casting conditions for strand casting a variety of steels at high withdrawal rate.
    Download PDF (2014K)
  • Sumio SHIOMI, Masafumi MAEDA, Nobuo SANO, Yukio MATSUSHITA
    1979 Volume 65 Issue 14 Pages 2032-2037
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    The present study was carried out to search for the possibility of the separate recovery of iron and phosphorus as gas from BOF slag by using graphite crucible or graphite powder with the presence of tin bath, which is considered to enhance the activity of phosphorus in iron reduced from slag or not to absorb the phosphorus vapor readily.
    When the slag was reduced by graphite crucible, being in contact wtih tin bath, the phosphorus reduced from slag was carried away by CO explosively generated on the reduction of iron oxide. When graphite powder was used as reductant instead, 78% of phosphorus was removed from slag, only 3% of which was absorbed into the tin bath and the rest left the system as gas. The extent of gaseous dephosphorization was observed to depend on the mode of contact between slag and reductant as well as the amount of the latter.
    Download PDF (1101K)
  • Hirowo G. SUZUKI, Satoshi NISHIMURA, Shigehiro YAMAGUCHI
    1979 Volume 65 Issue 14 Pages 2038-2046
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Hot ductility in steels was studied. Special emphases were placed on the effects of thermal history, strain rate and fracture mode in order to clarify the sensitivity of surface cracking during both continuous casting operation and direct hot rolling.
    There exist three temperature regions where typical embrittlement is noticed, i. e, Tm-1200 (I), 1 200-900 (II), and-700°C (III). The cause of embrittlement in the region I is the existence of residual liquid film along the dendritic interfaces. The ductility was found to be indepent of the strain rate. In the region II, the precipitation of finely distributed oxy-sulfides at the austenite grain boundary weakens the boundary strength, and thus overaging treatment such as slow cooling, holding for certain time, or slow rate of straining result in good ductility. On the other hand, the embrittlement in the III region is manifested by the slower strain rate of test. Controlling factors of this embrittlement are precipitation of oxides, sulfides and nitrides, precipitation of proeutectoid ferrite film along austenite grain boundary as well as grain boundary sliding. Detailed mechanism was discussed.
    Download PDF (11635K)
  • Michio INAGAKI, Takayoshi KASUGAI, Kazuo EI, Tomokazu GODAI, Osamu TAN ...
    1979 Volume 65 Issue 14 Pages 2047-2056
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Effect of welding conditions and a long term heat-treatment at 650°C on metallurgical changes in austenitic stainless steels (SUS 304 and SUS 316) weld metals have been investigated. Results were as follows; 1) The solidifying structure at center parts of weld metals tend to grow parallel to the direction of plate thickness of the 1 pass 1 layer welded joint. 2) δ-ferrite forms in the order to the solidifying directions. 3) δ-ferrite changes those morphologies from granular and rod-like shape to net-like shape with increase of the amount of δ-ferrite. In the case of large amount δ-ferrite, this net-like δ-ferrite takes the form into densely three-dimentional network in the inner part of each pass. 4) There is no δ-ferrite network in the boundary zone between pass and the following pass, because δ-ferrite in these boundary zone are mixed granular and rod-like shape. 5) Networks of δ-ferrite in high heat input weld metals are larger than that in low heat input weld metals. 6) Carbides and δ phase precipitate in δ-ferrite subjected to heating for a long term at 650°C. 7) Carbides and δ phase take the form of network with a long term heating at 650°C in the weld metal containing a large volume of δ-ferrite.
    From above results and the correlated research results of creep test and notch toughness of austenitic stainless steel weld metals subjected to a long term heat-treatment, it is considered that the following processes are advisable for the prevention measure of material worse at high temperature; 1) Selecting of the weld metals in which have the amount of δ-ferrite under about 5%, for the reason of dispertion of δ-ferrite and for destruction of δ-ferrite networks. 2) Making use of 2 pass 1 layer welding sequence to disperse the solidifying direction and applying the low heat input welding process to destroy δ-ferrite networks.
    Download PDF (9184K)
  • Yoshio SHIBUYA, Yoshiaki IMAZAWA, Kazutoshi KUWANA
    1979 Volume 65 Issue 14 Pages 2057-2066
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    A study has been made of the sliding wear characteristics of boride layer formed on S45C steel by boriding. As compared with the unborided S45C steel, the wear resistance of boride layer was very large in sliding velocity region between 0.1 and 4.5 m/s. It was on a level with the wear resistance of SKS3 in sliding velocity region between 0.1 and 1.0 m/s, and it was larger than that of SKS3 in sliding velocity region between 2.0 and 4.5 m/s. In the wear characteristics of boride layer, the oxidative wear was preferentially observed in sliding velocity region between 0.1 and 1.0 m/s. The maximum wear rate was observed 1.4 or 2.0 m/s in sliding velocity and in this region the mechanical wear was observed. It was considered that the melting wear was caused in sliding velocity above 3.0 m/s. The metallic debris caused by sliding wear with borided steel-low carbon steel was produced even in the slow sliding velocity of 0.1 m/s, and it increased with the increase of sliding velocity. It was considered that the wear loss of boride layer was largely influenced by the metallic debris contents produced with sliding wear of borided steel-low carbon steel. The oxide that were produced in the oxidative wear region restrained the adhesion between frictional surfaces. It was confirmed by the X-ray diffraction that the oxide consisted mainly of Fe3O4 and α-Fe2O3.
    Download PDF (13179K)
  • Hiroshi TAKECHI, Kazuo NAMBA, Koichi KAWASAKI, Keizo FUJIWARA
    1979 Volume 65 Issue 14 Pages 2067-2075
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Technique of the X-ray diffraction line profile analysis has been applied to the study of fatigue damage below the surface of the work and the backup rolls of cold strip mill and the backup rolls of hot strip mill. Half value breadth has been taken as a measure of fatiguing.
    Fatigued zone below the surface of rolls is well correlated with the half contact length of roll, L; 0.03 L in the work roll of cold strip mill and 0.1 L in the other rolls. Changes in the half value breadth with increase in cycles of roll contact differ in accordance with the surface hardness of the rolls: continued cycling results in decrease of the half value breadth at surface in hard rolls (Hs≥60) and increase in soft rolls (Hs≤50). The technique of X-ray study of fatigue can be extended to prediction and prevention of accidental failure of rolls due to fatigue fracture such as spalling. Furthermore the amount of surface dressing at regular maintenance of rolls can be saved significantly on the basis of accurate evaluation of the depth of fatigue damaged zone.
    Download PDF (5518K)
  • Shin YOKOI, Sadao IKEDA, Hiroshi ITO, Eiji BABA
    1979 Volume 65 Issue 14 Pages 2076-2087
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Download PDF (2392K)
  • Kokichi TAKAHASHI
    1979 Volume 65 Issue 14 Pages 2088-2096
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Download PDF (9670K)
  • Shoji IWAOKA, Nobuo OHASHI
    1979 Volume 65 Issue 14 Pages 2097-2103
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Download PDF (1380K)
  • Gentaro MATSUMURA
    1979 Volume 65 Issue 14 Pages 2104-2105
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Download PDF (321K)
  • Micho INOUYE
    1979 Volume 65 Issue 14 Pages 2106-2107
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Download PDF (2425K)
  • [in Japanese], [in Japanese], [in Japanese], [in Japanese], [in Japane ...
    1979 Volume 65 Issue 14 Pages 2108-2112
    Published: December 01, 1979
    Released: February 22, 2010
    JOURNALS FREE ACCESS
    Download PDF (1343K)