巻号一覧
43 巻, 6 号
選択された号の論文の15件中1～15を表示しています
- |<
- <
- 1
- >
- >|
-
中前 勝彦, 西野 孝, 松本 恒隆, 高橋 泰洋1987 年 43 巻 6 号 p. 277-282
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーElastic moduli of crystalline regions of poly (ether ether ketone)_??_(PEEK) in the direction parallel (El) and perpendicular (Et) to the chain axis were determined by X-ray diffraction. The observed moduli Et are as follows; (110); Et=5.9 GPa, (200); Et=4.2 GPa, (020); Et=5.0 GPa. The Et value for the (200) plane is nearly equal to that of polyethylene (ca. 4 GPa). This means that there is no especially strong interaction other than dispersion forces in this direction. But Et values for the (020), (110) planes are somewhat large. This is considered to be due to the dipole-dipole interactions between ether (carbonyl) linkages, since these functional groups are superposed upon each other in these directions. On the other hand, different orders of meridional reflections give different El values (31, 57, 71 GPa for (002), (006) and (008) plane, respectively). This phenomena may be due to the increase of the crystallite size by the applied stress. Judging from the similarity to the calculated El value (69 GPa), it seems that the El value for the (008) plane (71 GPa) is valid, from which the force required to stretch a molecule by 1% can be calculated as 1.64×10-5 dyne.抄録全体を表示PDF形式でダウンロード (1385K) -
石川 博, 奈倉 正宣, 土屋 陽一郎1987 年 43 巻 6 号 p. 283-287
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーInvestigations have been made on the fine structure and the physical properties of the blend film composed of silk sericin of Bombyx mori and poly (vinyl alcohol). The microphase separated structure was found in the blend film. The interfacial region between two phases may consist of PVA-sericin complex. The complex formation seems to yield the increase of fracture strain and the decrease of elongation at high temperature.抄録全体を表示PDF形式でダウンロード (827K) -
戸倉 清一, 西村 紳一郎, 西 則雄, 中村 邦男, 指輪 仁之, 長谷川 長俊, 瀬尾 寛1987 年 43 巻 6 号 p. 288-293
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーキチン繊維より良好な糸質の繊維を得るため,種々の脱アセチル化キチン(DAC)を調製した。これらの紡糸ではCuSO4-NH4OH,アルコール製水酸化ナトリウム及びCuSO4-H2SO4の3種の凝固系が見出され,いずれもよく似た糸質の繊維が得られた。しかし,繊維表面への蛋白質固定化では, CuSO4-NH4OH凝固系がより良好な結果を与えた。得られた種々のDAC繊維の糸質はキチンのそれより優れていたが特に湿潤時の引張り強度及び結節強度がキチン繊維やアルキルキチン繊維に比べ大巾に改善されていた。抄録全体を表示PDF形式でダウンロード (871K) -
上甲 恭平, 古賀 城一1987 年 43 巻 6 号 p. 294-299
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリー未延伸,延伸羊毛繊維への分散染料の染色性を前報で報告した酸性染料による結果と比較検討し,結果を羊毛の構造変化と関係づけて考察した。
等温吸着曲線は未延伸,延伸繊維いずれも直線型の等温線であったが,平衡染着量は未延伸,延伸繊維の間に明らかな差が認められ延伸倍率の増加とともに増大した。また,染色熱は延伸処理による構造変化に関係なく一定の値が得られた。これらのことから延伸処理による平衡染着量の増大はケラチン鎖のコンホメーション変化に伴う結合サイトへの相互作用の変化によるものではなく,主として延伸に伴う有効染着容積の変化に起因するものと考察した。
一方,初期収着に対する表面障壁は酸性染料の場合とは異なり未延伸,延伸処理繊維のいずれにおいても認められず,繊維内部への収着速度も延伸処理による影響をほとんど受けないことがわかった。抄録全体を表示PDF形式でダウンロード (390K) -
顔 明雄, 張 耀明, 陳 建智1987 年 43 巻 6 号 p. 300-304
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーThis paper deals with the durable-press finishing for cotton fabrics using dimethylol ethyleneurea (DMEU) condensates having various chain lengths. The results obtained at various concentrations of the crosslinking agents showed that such agents with shorter chain lengths improved dry crease recovery angle whereas wet crease recovery angle was not affected by chain length.
A better balance between the dry and wet crease recovery angles was obtained by increasing crosslinking agent content and also by using the crosslinking agents with the shorter chain length.
The increase of dry and wet crease resistance caused a decrease in the tensile strength of finished fabrics. A small decrease in tensile strength was observed when crosslinking agents with longer chain length were used. The effects of the chain length of crosslinking agents on the physical properties of durable-press cotton fabrics may be explained as the crosslinking structure formed in the finished cotton fabrics.抄録全体を表示PDF形式でダウンロード (341K) -
顔 明雄1987 年 43 巻 6 号 p. 305-312
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーThe crosslinking structure and physical properties of cotton fabrics treated with dimethylol ethyleneurea (DMEU) condensates having different chain lengths were investigated.
It was found that the reaction of the reagent changed at 4% of the concentration. A crosslinking reaction between the reagent and cellulose was the main reaction below 4%, whereas the condensation reaction between the reagents occurred predominantly at the concentration above 4%.
The dry crease recovery angle was related to the product of the number of crosslinks and the square root of crosslinking length. The wet crease recovery angle was related to the product of the crosslinking length and the number of crosslinks.
Accordingly, when the crosslinking length was shorter, the dry crease recovery angle became larger and the balance between dry and wet crease recovery was improved.
It was also found that the tensile strength was directly related to the number of crosslinks: fewer crosslinks and longer crosslinking length increased the retention of tensile strength when nitrogen content of treated fabrics was the same.抄録全体を表示PDF形式でダウンロード (520K) -
幾田 信生, 安部 郁夫, 平嶋 恒亮, 坂本 敏夫, 神山 孝久1987 年 43 巻 6 号 p. 313-319
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーガラス繊維強化プラスチックスの積層板に用いられるE-ガラスクロスのシランカップリング処理を評価する方法として,フーリエ変換赤外分光法の中でも最も簡便な透過法を試みることにした。シランカップリング剤, γ-アニリノプロピルトリメトキシシラン(AnPS)で処理したガラスクロスをそのまま測定試料として供した。測定したスペクトルからクロスによる赤外光の散乱および吸収の寄与を除くために,元のクロスで得たスペクトルを参照として差スペクトルを求めた。その結果, 1200cm-1以下の領域を除いてAnPSによる吸収に相当するスペクトルを得た。その際,シラン処理溶液中の酸によるガラスへの侵食が著しくシロキサン吸収帯域に影響した。このため,参照として同等の酸を含む溶液で処理したクロスを用いたところ全くシロキサンによる吸収帯は出現しなかった。これらの結果はカップリング剤がガラス上で形成するシロキサンを本法では認識できないことを示唆している。また, 1200cm-1以下のAnPSによる吸収帯もほとんど見られなかった。これらの現象はガラス自身の吸収帯付近における異常分散に起因するものと推測した。抄録全体を表示PDF形式でダウンロード (443K) -
山本 孝, 土定 育英, 松本 義隆, 新宅 救徳1987 年 43 巻 6 号 p. 320-328
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーFactors affecting the surface shape of a hard-twist-yarn fabric were experimentally examined in terms of the weaving and heat-set conditions, and particularly the crystallinity of the original fibers. The results obtained are as follows:
(1) The number of ribs increases in proportion to the torque which remains after the twist set was given to the yarns; the increasing rate is high (or low) at the set temperature higher (or lower) than the annealing temperature of the original yarns.
(2) The height of ribs depends on the torque and shrinking force generated in the yarns when the fabrics are scoured.
(3) The higher the crystallinity of the fibers, the larger the yarn torque is. This gives rise to a large number of thinner ribs.
(4) The number of ribs increases and the rib height decreases with increasing twisting tension of the yarn. The rib height also increases with increasing twist-set tension applied to yarns.抄録全体を表示PDF形式でダウンロード (1176K) -
韓 礼元, 脇田 登美司, 高岸 徹1987 年 43 巻 6 号 p. 329-332
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーポリエチレンテレフタレート繊維およびタフタを連続式高圧スチーマで処理し,分散染料(C. I. Disperse Violet 1およびYellow 7)に対する固着率を乾熱および過熱蒸気で処理したものと比較した。さらに,高圧スチーミング,過熱スチーミングおよび乾熱処理したポリエチレンテレフタレート繊維の内部構造の変化を, X線回折,結晶化度および飽和染着量によって調べた。固着率は,乾熱処理<過熱スチーミング<高圧スチーミングの順に増大した。また,過熱スチーミングおよび乾熱処理の場合よりも,高圧スチーミングの場合のほうが結晶化度と結晶粒子の大きさは増大するが,飽和染着量にはほとんど差は認められなかった。抄録全体を表示PDF形式でダウンロード (668K) -
小池 三枝1987 年 43 巻 6 号 p. P200-P204
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーPDF形式でダウンロード (1065K) -
藤原 康晴1987 年 43 巻 6 号 p. P205-P209
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーPDF形式でダウンロード (1059K) -
オレセン ビアーネヴィルケンス, 長谷部 ヤエ1987 年 43 巻 6 号 p. P210-P221
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーPDF形式でダウンロード (2104K) -
南本 珠己1987 年 43 巻 6 号 p. P222-P227
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーPDF形式でダウンロード (970K) -
山崎 信寿1987 年 43 巻 6 号 p. P228-P232
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーPDF形式でダウンロード (1012K) -
國本 由人, 原山 金三1987 年 43 巻 6 号 p. P233-P239
発行日: 1987/06/10
公開日: 2008/11/28
ジャーナル フリーPDF形式でダウンロード (950K)
- |<
- <
- 1
- >
- >|